Densification mechanism and microstructure characteristics of nano- and micro- crystalline alumina by high-pressure and low temperature sintering

Fully dense ceramics with retarded grain growth can be attained effectively at relatively low temperatures using a high-pressure sintering method. However, there is a paucity of in-depth research on the densification mechanism, grain growth process, grain boundary characterization, and residual stress. Using a strong, reliable die made from a carbon-fiber-reinforced carbon (C_f/C) composite for spark plasma sintering, two kinds of commercially pure α-Al₂O₃ powders, with average particle sizes of 220 nm and 3 μm, were sintered at relatively low temperatures and under high pressures of up to 200 MPa. The sintering densification temperature and the starting threshold temperature of grain growth (T_sg) were determined by the applied pressure and the surface energy relative to grain size, as they were both observed to increase with grain size and to decrease with applied pressure. Densification with limited grain coarsening occurred under an applied pressure of 200 MPa at 1050 °C for the 220 nm Al₂O₃ powder and 1400 °C for the 3 μm Al₂O₃ powder. The grain boundary energy, residual stress, and dislocation density of the ceramics sintered under high pressure and low temperature were higher than those of the samples sintered without additional pressure. Plastic deformation occurring at the contact area of the adjacent particles was proved to be the dominant mechanism for sintering under high pressure, and a mathematical model based on the plasticity mechanics and close packing of equal spheres was established. Based on the mathematical model, the predicted relative density of an Al₂O₃ compact can reach ～80 % via the plastic deformation mechanism, which fits well with experimental observations. The densification kinetics were investigated from the sintering parameters, i.e., the holding temperature, dwell time, and applied pressure. Diffusion, grain boundary sliding, and dislocation motion were assistant mechanisms in the final stage of sintering, as indicated by the stress exponent and the microstructural evolution. During the sintering of the 220 nm alumina at 1125 °C and 100 MPa, the deformation tends to increase defects and vacancies generation, both of which accelerate lattice diffusion and thus enhance grain growth.     

Water vapor volatilization and oxidation induced surface cracking of environmental barrier coating systems: A numerical approach

A numerical model is developed for surface crack propagation in brittle ceramic coatings, aiming at the intrinsic failure of rare-earth silicate environmental barrier coating systems (EBCs) under combustion conditions in advanced gas turbines. The main features of progressive degradation of EBCs in such conditions are captured, including selective silica vaporization in the top coat due to exposure to water vapor, diffusion path-dependent bond coat oxidation, as well as crack propagation during cyclic thermal loading. In light of these features, user-defined subroutines are implemented in finite element analysis, where surface crack growth is simulated by node separation. Numerical results are validated by existing experimental data, in terms of monosilicate layer thickening, thermal oxide growth, and fracture behaviors. The experimentally observed quasi-linear oxidation in the early stage is also elucidated. Furthermore, it is suggested that surface crack undergoes rapid propagation in the late stage of extended thermal cycling in water vapor and leads to catastrophic failure, driven by both thermal mismatch and oxide growth stresses. The latter is identified as the dominant mechanism of penetration. Based on detailed analyses of failure mechanisms, the optimization strategy of EBCs composition is proposed, balancing the trade-off between mechanical compliance and erosion resistance.     

N-乙氧基羰基-N,N',N'-三甲基胍高效液相色谱分析方法研究

N-乙氧基羰基-N,N',N'-三甲基胍(简称:三甲基胍)是合成高选择性森林除草剂环嗪酮的主要中间体,国内未见高效液相色谱检测方法的报道,我们采用反相高效液相色谱法对三甲基胍进行了定量分析研究,流动相为:V(水)︰V(乙腈)=90︰10,使用ODSC18为填料的不锈钢柱及具可变波长的紫外检测器.本方法的变异系数为0.19％,标准偏差为0.15,平均回收率为99.56％,经优化后的检测方法简捷、准确,能满足工业化产品定量检测需要.     

Meticulously tailoring phase boundary in KNN-based ceramics to enhance piezoelectricity and temperature stability

Although KNN-based ceramics with high electrical properties are obtained through a variety of strategies, the temperature sensitivity is still one of the key technical bottlenecks hindering practical applications. Here, we use a new strategy, meticulously tailoring phase boundary, to refine the ferroelectric boundary of KNN-based ceramics, leading to high piezoelectricity companied with improving temperature stability. The highest d₃₃ value in this system reaches 501 pC/N with a T_C ∼ 240°C, whereas a large strain of ∼0.134% can be kept with 10% lower deterioration until 100°C. The origin of high piezoelectricity is mainly attributed to the well-preserved multiphase coexistence and the appearance of nanodomains, which greatly facilitate the polarization rotation. Instead of the changed intrinsic thermal insensitivity, the precision phase boundary engineering plays an important role in strengthening the temperature stability of electric-induced strain. This work provides a simple and effective method to obtain both high electrical properties and excellent thermal stability in KNN-based ceramics, which is expected to promote the practical applications in the future.     

综合设计性实验在药物分析学实验中对学生综合能力的培养

《药物分析学实验》是药学专业的一门独立必修课程,是药学科学领域中的一个重要组成部分,具有较强的实践性和综合性,旨在培养学生综合运用所学知识分析药品质量的能力.综合设计性实验作为《药物分析学实验》的重要组成部分,对学生实践操作能力,发现问题、分析问题、解决问题的能力,创新能力,应用能力,团结协作能力,劳动素养等综合能力的培养具有极其重要的意义.     

Facile Synthesis of Fluorine Doped Rutile TiO2 Nanorod Arrays for Photocatalytic Removal of Formaldehyde

Catalysis Letters - It is crucial to explore a facile synthesis of rutile TiO2 nanorods anchored at carbon cloth at low temperature for applicable air purifier. Herein, antler-like TiO2 rectangular...     

Improving water retention of chicken breast meats by CaCl2 combined with pulsed electric fields

Frozen poultry meat is the most widely consumed animal-based food. However, water loss often leads to quality loss of poultry meat. Therefore, the present study sought to investigate the combined effect of calcium chloride (CaCl₂) and pulsed electric fields (PEF) treatment on chicken breast meats and the mechanisms underlying protein degradation. The results showed that the synergistic effect was superior to the single treatment. Compared with the untreated group, the combination of CaCl₂ and PEF increased water holding capacity of chicken breast meats by 16.61% and decreased cooking loss by 28.93%. Low-field nuclear magnetic resonance (LF-NMR) results indicated that the synergistic treatment promoted water molecules' binding capacity in myofibrils of poultry meat, which exhibited higher immobilised water. Additionally, the combination of CaCl₂ and PEF led to increased degradation of proteins of high-molecular weight and surface hydrophobicity of myofibrillar protein. Furthermore, the extension of the protein molecule and microenvironmental changes promoted interaction between protein and water. In conclusion, the synergistic treatment of CaCl₂ and PEF enhanced water retention and improved physicochemical properties of the myofibrillar protein in chicken breast meats.